Aluminium (or aluminum in North American English) is a chemical element; it has chemical symbol Al and atomic number 13. It has a density lower than that of other common , about one-third that of steel. Aluminium has a great affinity towards oxygen, forming a protective layer of aluminium oxide on the surface when exposed to air. It visually resembles silver, both in its color and in its great ability to reflect light. It is soft, magnetism, and ductility. It has one stable isotope, 27Al, which is highly abundant, making aluminium the 12th-most abundant element in the universe. The radioactivity of 26Al leads to it being used in radiometric dating.
Chemically, aluminium is a post-transition metal in the boron group; as is common for the group, aluminium forms compounds primarily in the +3 oxidation state. The aluminium cation Al3+ is small and highly charged; as such, it has more polarizing power, and chemical bond formed by aluminium have a more covalent bond character. The strong affinity of aluminium for oxygen leads to the common occurrence of its oxides in nature. Aluminium is found on Earth primarily in rocks in the crust, where it is the third-most abundant element, after oxygen and silicon, rather than in the mantle, and virtually never as the free element. It is obtained industrially by mining bauxite, a sedimentary rock rich in aluminium minerals.
The discovery of aluminium was announced in 1825 by Danish physicist Hans Christian Ørsted. The first industrial production of aluminium was initiated by French chemist Henri Étienne Sainte-Claire Deville in 1856. Aluminium became much more available to the public with the Hall–Héroult process developed independently by French engineer Paul Héroult and American engineer Charles Martin Hall in 1886, and the mass production of aluminium led to its extensive use in industry and everyday life. In the First and Second World Wars, aluminium was a crucial strategic resource for aviation. In 1954, aluminium became the most produced non-ferrous metal, surpassing copper. In the 21st century, most aluminium was consumed in transportation, engineering, construction, and packaging in the United States, Western Europe, and Japan.
Despite its prevalence in the environment, no living organism is known to Metabolism aluminium salts, but this aluminium is well tolerated by plants and animals. Because of the abundance of these salts, the potential for a biological role for them is of interest, and studies are ongoing.
All other isotopes of aluminium are radioactive. The most stable of these is 26Al: while it was present along with stable 27Al in the interstellar medium from which the Solar System formed, having been produced by stellar nucleosynthesis as well, its half-life is only 717,000 years and therefore a detectable amount has not survived since the formation of the planet. However, minute traces of 26Al are produced from argon in the atmosphere by spallation caused by cosmic ray protons. The ratio of 26Al to 10Be has been used for radiodating of geological processes over 105 to 106 year time scales, in particular transport, deposition, sediment storage, burial times, and erosion. (2025). 9780521530170, Cambridge University Press. ISBN 9780521530170
Most meteorite scientists believe that the energy released by the decay of 26Al was responsible for the melting and differentiation of some asteroids after their formation 4.55 billion years ago.
The remaining isotopes of aluminium, with ranging from 21 to 43, all have half-lives well under an hour. Three metastable states are known, all with half-lives under a minute.
The density of aluminium is 2.70 g/cm3, about 1/3 that of steel, much lower than other commonly encountered metals, making aluminium parts easily identifiable through their lightness. Aluminium's low density compared to most other metals arises from the fact that its nuclei are much lighter, while difference in the unit cell size does not compensate for this difference. The only lighter metals are the metals of alkali metal and 2, which apart from beryllium and magnesium are too reactive for structural use (and beryllium is very toxic). Aluminium is not as strong or stiff as steel, but the low density makes up for this in the aerospace industry and for many other applications where light weight and relatively high strength are crucial.
Pure aluminium is quite soft and lacking in strength. In most applications various aluminium alloys are used instead because of their higher strength and hardness. The yield strength of pure aluminium is 7–11 MPa, while have yield strengths ranging from 200 MPa to 600 MPa. (1995). 9780340632079, Butterworth-Heinemann. ISBN 9780340632079
Aluminium is ductility, with a percent elongation of 50–70%,
and malleable allowing it to be easily drawn and extrusion. It is also easily machining and cast.
Aluminium is an excellent Heat conduction and electrical conductor, having around 60% the conductivity of copper, both thermal and electrical, while having only 30% of copper's density. Aluminium is capable of superconductor, with a superconducting critical temperature of 1.2 kelvin and a critical magnetic field of about 100 gauss (10 ). It is paramagnetic and thus essentially unaffected by static magnetic fields. The high electrical conductivity, however, means that it is strongly affected by alternating magnetic fields through the induction of eddy currents.
The underlying core under aluminium's valence shell is that of the preceding noble gas, whereas those of its heavier congeners gallium, indium, thallium, and nihonium also include a filled d-subshell and in some cases a filled f-subshell. Hence, the inner electrons of aluminium shield the valence electrons almost completely, unlike those of aluminium's heavier congeners. As such, aluminium is the most electropositive metal in its group, and its hydroxide is in fact more basic than that of gallium. Aluminium also bears minor similarities to the metalloid boron in the same group: AlX3 compounds are valence isoelectronic to BX3 compounds (they have the same valence electronic structure), and both behave as and readily form . Additionally, one of the main motifs of boron chemistry is regular icosahedral structures, and aluminium forms an important part of many icosahedral quasicrystal alloys, including the Al–Zn–Mg class.
Aluminium has a high chemical affinity to oxygen, which renders it suitable for use as a reducing agent in the thermite reaction. A fine powder of aluminium reacts explosively on contact with liquid oxygen; under normal conditions, however, aluminium forms a thin oxide layer (~5 nm at room temperature)John E. Hatch (1984). 9781615031696, American Society for Metals, Aluminum Association. ISBN 9781615031696
that protects the metal from further corrosion by oxygen, water, or dilute acid, a process termed passivation.
Aluminium is not attacked by oxidizing acids because of its passivation. This allows aluminium to be used to store reagents such as nitric acid, concentrated sulfuric acid, and some organic acids. (2025). 9783527306732, Wiley-VCH. ISBN 9783527306732
In hot concentrated hydrochloric acid, aluminium reacts with water with evolution of hydrogen, and in aqueous sodium hydroxide or potassium hydroxide at room temperature to form aluminates—protective passivation under these conditions is negligible. Aqua regia also dissolves aluminium. Aluminium is corroded by dissolved chlorides, such as common sodium chloride. The oxide layer on aluminium is also destroyed by contact with mercury due to amalgamation or with salts of some electropositive metals. As such, the strongest aluminium alloys are less corrosion-resistant due to galvanic cell reactions with alloyed copper, and aluminium's corrosion resistance is greatly reduced by aqueous salts, particularly in the presence of dissimilar metals.
Aluminium reacts with most nonmetals upon heating, forming compounds such as aluminium nitride (AlN), aluminium sulfide (Al2S3), and the aluminium halides (AlX3). It also forms a wide range of intermetallic compounds involving metals from every group on the periodic table.
In aqueous solution, Al3+ exists as the hexaaqua cation Al(H2O)63+, which has an approximate Ka of 10−5. Such solutions are acidic as this cation can act as a proton donor and progressively hydrolysis until a precipitate of aluminium hydroxide, Al(OH)3, forms. This is useful for clarification of water, as the precipitate nucleates on suspended particles in the water, hence removing them. Increasing the pH even further leads to the hydroxide dissolving again as aluminate, Al(H2O)2(OH)4−, is formed.
Aluminium hydroxide forms both salts and aluminates and dissolves in acid and alkali, as well as on fusion with acidic and basic oxides. This behavior of Al(OH)3 is termed amphoterism and is characteristic of weakly basic cations that form insoluble hydroxides and whose hydrated species can also donate their protons. One effect of this is that with weak acids are hydrolyzed in water to the aquated hydroxide and the corresponding nonmetal hydride: for example, aluminium sulfide yields hydrogen sulfide. However, some salts like aluminium carbonate exist in aqueous solution but are unstable as such; and only incomplete hydrolysis takes place for salts with strong acids, such as the halides, nitrate, and sulfate. For similar reasons, anhydrous aluminium salts cannot be made by heating their "hydrates": hydrated aluminium chloride is in fact not AlCl3·6H2O but Al(H2O)6Cl3, and the Al–O bonds are so strong that heating is not sufficient to break them and form Al–Cl bonds. This reaction is observed instead:
All four Halide are well known. Unlike the structures of the three heavier trihalides, aluminium fluoride (AlF3) features six-coordinate aluminium, which explains its involatility and insolubility as well as high heat of formation. Each aluminium atom is surrounded by six fluorine atoms in a distorted octahedron arrangement, with each fluorine atom being shared between the corners of two octahedra. Such {AlF6} units also exist in complex fluorides such as cryolite, Na3AlF6. AlF3 melts at and is made by reaction of aluminium oxide with hydrogen fluoride gas at .
With heavier halides, the coordination numbers are lower. The other trihalides are dimeric or with tetrahedral four-coordinate aluminium centers. Aluminium trichloride (AlCl3) has a layered polymeric structure below its melting point of but transforms on melting to Al2Cl6 dimers. At higher temperatures those increasingly dissociate into trigonal planar AlCl3 monomers similar to the structure of BCl3. Aluminium tribromide and aluminium triiodide form Al2X6 dimers in all three phases and hence do not show such significant changes of properties upon phase change. These materials are prepared by treating aluminium with the halogen. The aluminium trihalides form many addition compounds or complexes; their nature makes them useful as catalysis for the Friedel–Crafts reactions. Aluminium trichloride has major industrial uses involving this reaction, such as in the manufacture of and styrene; it is also often used as the precursor for many other aluminium compounds and as a reagent for converting nonmetal fluorides into the corresponding chlorides (a transhalogenation reaction).
Aluminium forms one stable oxide with the chemical formula Al2O3, commonly called alumina. It can be found in nature in the mineral corundum, α-alumina; there is also a γ-alumina phase. Its crystalline form, corundum, is very hard (Mohs hardness 9), has a high melting point of , has very low volatility, is chemically inert, and a good electrical insulator, it is often used in abrasives (such as toothpaste), as a refractory material, and in ceramics, as well as being the starting material for the electrolytic production of aluminium. Sapphire and ruby are impure corundum contaminated with trace amounts of other metals. The two main oxide-hydroxides, AlO(OH), are boehmite and diaspore. There are three main trihydroxides: bayerite, gibbsite, and nordstrandite, which differ in their crystalline structure (polymorphs). Many other intermediate and related structures are also known. Most are produced from ores by a variety of wet processes using acid and base. Heating the hydroxides leads to formation of corundum. These materials are of central importance to the production of aluminium and are themselves extremely useful. Some mixed oxide phases are also very useful, such as spinel (MgAl2O4), Na-β-alumina (NaAl11O17), and tricalcium aluminate (Ca3Al2O6, an important mineral phase in Portland cement).
The only stable under normal conditions are aluminium sulfide (Al2S3), selenide (Al2Se3), and telluride (Al2Te3). All three are prepared by direct reaction of their elements at about and quickly hydrolyze completely in water to yield aluminium hydroxide and the respective hydrogen chalcogenide. As aluminium is a small atom relative to these chalcogens, these have four-coordinate tetrahedral aluminium with various polymorphs having structures related to wurtzite, with two-thirds of the possible metal sites occupied either in an orderly (α) or random (β) fashion; the sulfide also has a γ form related to γ-alumina, and an unusual high-temperature hexagonal form where half the aluminium atoms have tetrahedral four-coordination and the other half have trigonal bipyramidal five-coordination.
Four – aluminium nitride (AlN), aluminium phosphide (AlP), aluminium arsenide (AlAs), and aluminium antimonide (AlSb) – are known. They are all III-V semiconductors isoelectronic to silicon and germanium, all of which but AlN have the zinc blende structure. All four can be made by high-temperature (and possibly high-pressure) direct reaction of their component elements.
well with most other metals (with the exception of most alkali metals and group 13 metals) and over 150 intermetallics with other metals are known. Preparation involves heating fixed metals together in certain proportion, followed by gradual cooling and annealing. Bonding in them is predominantly Metallic bonding and the crystal structure primarily depends on efficiency of packing.
There are few compounds with lower oxidation states. A few aluminium(I) compounds exist: AlF, AlCl, AlBr, and AlI exist in the gaseous phase when the respective trihalide is heated with aluminium, and at cryogenic temperatures. A stable derivative of aluminium monoiodide is the cyclic adduct formed with triethylamine, Al4I4(NEt3)4. Al2O and Al2S also exist but are very unstable. Very simple aluminium(II) compounds are invoked or observed in the reactions of Al metal with oxidants. For example, aluminium monoxide, AlO, has been detected in the gas phase after explosion and in stellar absorption spectra. More thoroughly investigated are compounds of the formula R4Al2 which contain an Al–Al bond and where R is a large organic ligand.
The industrially most important aluminium hydride is lithium aluminium hydride (LiAlH4), which is used as a reducing agent in organic chemistry. It can be produced from lithium hydride and aluminium trichloride. The simplest hydride, aluminium hydride or alane, is not as important. It is a polymer with the formula (AlH3) n, in contrast to the corresponding boron hydride that is a dimer with the formula (BH3)2.
Because of its strong affinity for oxygen, aluminium is almost never found in the elemental state; instead it is found in oxides or silicates. , the most common group of minerals in the Earth's crust, are aluminosilicates. Aluminium also occurs in the minerals beryl, cryolite, garnet, spinel, and turquoise. Impurities in Al2O3, such as chromium and iron, yield the ruby and sapphire, respectively. Native aluminium metal is extremely rare and can only be found as a minor phase in low oxygen fugacity environments, such as the interiors of certain volcanoes. Native aluminium has been reported in in the northeastern continental slope of the South China Sea. It is possible that these deposits resulted from Redox of tetrahydroxoaluminate Al(OH)4−.
Although aluminium is a common and widespread element, not all aluminium minerals are economically viable sources of the metal. Almost all metallic aluminium is produced from the ore bauxite (AlO x(OH)3–2 x). Bauxite occurs as a weathering product of low iron and silica bedrock in tropical climatic conditions. (1986). 9780716714569, W.H. Freeman. ISBN 9780716714569 In 2017, most bauxite was mined in Australia, China, Guinea, and India.
The nature of alum remained unknown. Around 1530, Swiss physician Paracelsus suggested alum was a salt of an earth of alum. In 1595, German doctor and chemist Andreas Libavius experimentally confirmed this. In 1722, German chemist Friedrich Hoffmann announced his belief that the base of alum was a distinct earth. In 1754, German chemist Andreas Sigismund Marggraf synthesized alumina by boiling clay in sulfuric acid and subsequently adding potash.
Attempts to produce aluminium date back to 1760. The first successful attempt, however, was completed in 1824 by Danish physicist and chemist Hans Christian Ørsted. He reacted anhydrous aluminium chloride with potassium amalgam, yielding a lump of metal looking similar to tin. He presented his results and demonstrated a sample of the new metal in 1825. In 1827, German chemist Friedrich Wöhler repeated Ørsted's experiments but did not identify any aluminium. (The reason for this inconsistency was only discovered in 1921.) He conducted a similar experiment in the same year by mixing anhydrous aluminium chloride with potassium (the Wöhler process) and produced a powder of aluminium. In 1845, he was able to produce small pieces of the metal and described some physical properties of this metal. For many years thereafter, Wöhler was credited as the discoverer of aluminium.
As Wöhler's method could not yield great quantities of aluminium, the metal remained rare; its cost exceeded that of gold. The first industrial production of aluminium was established in 1856 by French chemist Henri Etienne Sainte-Claire Deville and companions. Deville had discovered that aluminium trichloride could be reduced by sodium, which was more convenient and less expensive than potassium, which Wöhler had used. Even then, aluminium was still not of great purity and produced aluminium differed in properties by sample. Because of its electricity-conducting capacity, aluminium was used as the cap of the Washington Monument, completed in 1885, the tallest building in the world at the time. The non-corroding metal cap was intended to serve as a lightning rod peak.
The first industrial large-scale production method was independently developed in 1886 by French engineer Paul Héroult and American engineer Charles Martin Hall; it is now known as the Hall–Héroult process. The Hall–Héroult process converts alumina into metal. Austrian chemist Carl Joseph Bayer discovered a way of purifying bauxite to yield alumina, now known as the Bayer process, in 1889. Modern production of aluminium is based on the Bayer and Hall–Héroult processes.
As large-scale production caused aluminium prices to drop, the metal became widely used in jewelry, eyeglass frames, optical instruments, tableware, and Aluminium foil, and other everyday items in the 1890s and early 20th century. Aluminium's ability to form hard yet light alloys with other metals provided the metal with many uses at the time. During World War I, major governments demanded large shipments of aluminium for light strong airframes; during World War II, demand by major governments for aviation was even higher.
From the early 20th century to 1980, the aluminium industry was characterized by Cartel, as aluminium firms colluded to keep prices high and stable. The first aluminium cartel, the Aluminium Association, was founded in 1901 by the Pittsburgh Reduction Company (renamed Alcoa in 1907) and Alusuisse. The British Aluminium Company, Produits Chimiques d’Alais et de la Camargue, and Société Electro-Métallurgique de Froges also joined the cartel.
By the mid-20th century, aluminium had become a part of everyday life and an essential component of housewares. In 1954, production of aluminium surpassed that of copper, historically second in production only to iron, making it the most produced non-ferrous metal. During the mid-20th century, aluminium emerged as a civil engineering material, with building applications in both basic construction and interior finish work, and increasingly being used in military engineering, for both airplanes and land armor vehicle engines. Earth's first artificial satellite, launched in 1957, consisted of two separate aluminium semi-spheres joined and all subsequent space vehicles have used aluminium to some extent. The aluminium can was invented in 1956 and employed as a storage for drinks in 1958.
Throughout the 20th century, the production of aluminium rose rapidly: while the world production of aluminium in 1900 was 6,800 metric tons, the annual production first exceeded 100,000 metric tons in 1916; 1,000,000 tons in 1941; 10,000,000 tons in 1971. In the 1970s, the increased demand for aluminium made it an exchange commodity; it entered the London Metal Exchange, the oldest industrial metal exchange in the world, in 1978. The output continued to grow: the annual production of aluminium exceeded 50,000,000 metric tons in 2013.
The real price for aluminium declined from $14,000 per metric ton in 1900 to $2,340 in 1948 (in 1998 United States dollars). Extraction and processing costs were lowered over technological progress and the scale of the economies. However, the need to exploit lower-grade poorer quality deposits and the use of fast increasing input costs (above all, energy) increased the net cost of aluminium; the real price began to grow in the 1970s with the rise of energy cost. Production moved from the industrialized countries to countries where production was cheaper. Production costs in the late 20th century changed because of advances in technology, lower energy prices, exchange rates of the United States dollar, and alumina prices. The BRIC countries' combined share in primary production and primary consumption grew substantially in the first decade of the 21st century. China is accumulating an especially large share of the world's production thanks to an abundance of resources, cheap energy, and governmental stimuli; it also increased its consumption share from 2% in 1972 to 40% in 2010. In the United States, Western Europe, and Japan, most aluminium was consumed in transportation, engineering, construction, and packaging. In 2021, prices for industrial metals such as aluminium have soared to near-record levels as energy shortages in China drive up costs for electricity.
One example was Essai sur la Nomenclature chimique (July 1811), written in French by a Swedish chemist, Jöns Jacob Berzelius, in which the name aluminium is given to the element that would be synthesized from alum.. (Another article in the same journal issue also refers to the metal whose oxide is the basis of sapphire, i.e. the same metal, as to aluminium.). A January 1811 summary of one of Davy's lectures at the Royal Society mentioned the name aluminium as a possibility. The next year, Davy published a chemistry textbook in which he used the spelling aluminum. Both spellings have coexisted since. Their usage is currently regional: aluminum dominates in the United States and Canada; aluminium is prevalent in the rest of the English-speaking world.
Ludwig Wilhelm Gilbert had proposed Thonerde-metall, after the German "Thonerde" for alumina, in his Annalen der Physik but that name never caught on at all even in Germany. Joseph W. Richards in 1891 found just one occurrence of argillium in Swedish, from the French "argille" for clay. The French themselves had used aluminium from the start. However, in England and Germany Davy's spelling aluminum was initially used; until German chemist Friedrich Wöhler published his account of the Wöhler process in 1827 in which he used the spelling aluminium, which caused that spelling's largely wholesale adoption in England and Germany, with the exception of a small number of what Richards characterized as "patriotic" English chemists that were "averse to foreign innovations" who occasionally still used aluminum.
Most scientists throughout the world used in the 19th century; and it was entrenched in several other European languages, such as French language, German language, and Dutch language.
In 1828, an American lexicographer, Noah Webster, entered only the aluminum spelling in his American Dictionary of the English Language. In the 1830s, the spelling gained usage in the United States; by the 1860s, it had become the more common spelling there outside science. In 1892, Hall used the spelling in his advertising handbill for his new electrolytic method of producing the metal, despite his constant use of the spelling in all the patents he filed between 1886 and 1903. It is unknown whether this spelling was introduced by mistake or intentionally, but Hall preferred aluminum since its introduction because it resembled platinum, the name of a prestigious metal. By 1890, both spellings had been common in the United States, the spelling being slightly more common; by 1895, the situation had reversed; by 1900, aluminum had become twice as common as aluminium; in the next decade, the spelling dominated American usage. In 1925, the American Chemical Society adopted this spelling.
The International Union of Pure and Applied Chemistry (IUPAC) adopted aluminium as the standard international name for the element in 1990. In 1993, they recognized aluminum as an acceptable variant; the most recent 2005 edition of the IUPAC nomenclature of inorganic chemistry also acknowledges this spelling. IUPAC official publications use the spelling as primary, and they list both where it is appropriate.
The production of aluminium starts with the extraction of bauxite rock from the ground. The bauxite is processed and transformed using the Bayer process into alumina, which is then processed using the Hall–Héroult process, resulting in the final aluminium.
Aluminium production is highly energy-consuming, and so the producers tend to locate smelters in places where electric power is both plentiful and inexpensive. Production of one kilogram of aluminium requires 7 kilograms of oil energy equivalent, as compared to 1.5 kilograms for steel and 2 kilograms for plastic. As of 2024, the world's largest producers of aluminium were China, Russia, India, Canada, and the United Arab Emirates, while China is by far the top producer of aluminium with a world share of over 55%.
According to the International Resource Panel's Metal Stocks in Society report, the global per capita stock of aluminium in use in society (i.e. in cars, buildings, electronics, etc.) is . Much of this is in more-developed countries ( per capita) rather than less-developed countries ( per capita).
After this reaction, the slurry is at a temperature above its atmospheric boiling point. It is cooled by removing steam as pressure is reduced. The bauxite residue is separated from the solution and discarded. The solution, free of solids, is seeded with small crystals of aluminium hydroxide; this causes decomposition of the Al(OH)4− ions to aluminium hydroxide. After about half of aluminium has precipitated, the mixture is sent to classifiers. Small crystals of aluminium hydroxide are collected to serve as seeding agents; coarse particles are converted to alumina by heating; the excess solution is removed by evaporation, (if needed) purified, and recycled.
Anodes of the electrolysis cell are made of carbon—the most resistant material against fluoride corrosion—and either bake at the process or are prebaked. The former, also called Söderberg anodes, are less power-efficient and fumes released during baking are costly to collect, which is why they are being replaced by prebaked anodes even though they save the power, energy, and labor to prebake the cathodes. Carbon for anodes should be preferably pure so that neither aluminium nor the electrolyte is contaminated with ash. Despite carbon's resistivity against corrosion, it is still consumed at a rate of 0.4–0.5 kg per each kilogram of produced aluminium. Cathodes are made of anthracite; high purity for them is not required because impurities leach only very slowly. The cathode is consumed at a rate of 0.02–0.04 kg per each kilogram of produced aluminium. A cell is usually terminated after 2–6 years following a failure of the cathode.
The Hall–Heroult process produces aluminium with a purity of above 99%. Further purification can be done by the Hoopes process. This process involves the electrolysis of molten aluminium with a sodium, barium, and aluminium fluoride electrolyte. The resulting aluminium has a purity of 99.99%.
Electric power represents about 20 to 40% of the cost of producing aluminium, depending on the location of the smelter. Aluminium production consumes roughly 5% of electricity generated in the United States. Because of this, alternatives to the Hall–Héroult process have been researched, but none has turned out to be economically feasible.
White dross from primary aluminium production and from secondary recycling operations still contains useful quantities of aluminium that can be extracted industrially. The process produces aluminium billets, together with a highly complex waste material. This waste is difficult to manage. It reacts with water, releasing a mixture of gases including, among others, acetylene, hydrogen sulfide and significant amounts of ammonia. Despite these difficulties, the waste is used as a filler in Asphalt concrete and concrete. Its potential for hydrogen production has also been considered and researched.
Aluminium is almost always alloyed, which markedly improves its mechanical properties, especially when tempered. For example, the common and beverage cans are alloys of 92% to 99% aluminium. The main alloying agents for both wrought and cast aluminium are copper, zinc, magnesium, manganese, and silicon (e.g., duralumin) with the levels of other metals in a few percent by weight.
The major uses for aluminium are in:
Several sulfates of aluminium have industrial and commercial application. Aluminium sulfate (in its hydrate form) is produced on the annual scale of several millions of metric tons. About two-thirds is consumed in water treatment. The next major application is in the manufacture of paper. It is also used as a mordant in dyeing, in pickling seeds, deodorizing of mineral oils, in leather tanning, and in production of other aluminium compounds. Two kinds of alum, ammonium alum and potassium alum, were formerly used as mordants and in leather tanning, but their use has significantly declined following availability of high-purity aluminium sulfate. Anhydrous aluminium chloride is used as a catalyst in chemical and petrochemical industries, the dyeing industry, and in synthesis of various inorganic and organic compounds. Aluminium hydroxychlorides are used in purifying water, in the paper industry, and as antiperspirants. Sodium aluminate is used in treating water and as an accelerator of solidification of cement.
Many aluminium compounds have niche applications, for example:
During the 1988 Camelford water pollution incident, people in Camelford had their drinking water contaminated with aluminium sulfate for several weeks. A final report into the incident in 2013 concluded it was unlikely that this had caused long-term health problems.
Aluminium has been suspected of being a possible cause of Alzheimer's disease, but research into this for over 40 years has found, , no good evidence of causal effect.
Aluminium increases estrogen-related gene expression in human breast cancer cells cultured in the laboratory.
In very high doses, aluminium is associated with altered function of the blood–brain barrier.
A small percentage of people have contact allergy to aluminium and experience itchy red rashes, headache, muscle pain, joint pain, poor memory, insomnia, depression, asthma, irritable bowel syndrome, or other symptoms upon contact with products containing aluminium.
Exposure to powdered aluminium or aluminium welding fumes can cause pulmonary fibrosis. Fine aluminium powder can ignite or explode, posing another workplace hazard.
Consumption of , antiperspirants, , and cosmetics provide possible routes of exposure. Consumption of acidic foods or liquids with aluminium enhances aluminium absorption, and maltol has been shown to increase the accumulation of aluminium in nerve and bone tissues.
Acidic precipitation is the main natural factor to mobilize aluminium from natural sources and the main reason for the environmental effects of aluminium; however, the main factor of presence of aluminium in salt and freshwater are the industrial processes that also release aluminium into air.
In water, aluminium acts as a toxiс agent on gill-breathing animals such as fish when the water is acidic, in which aluminium may precipitate on gills, which causes loss of Blood plasma- and hemolymph ions leading to Osmoregulation failure. Organic complexes of aluminium may be easily absorbed and interfere with metabolism in mammals and birds, even though this rarely happens in practice.
Aluminium is primary among the factors that reduce plant growth on acidic soils. Although it is generally harmless to plant growth in pH-neutral soils, in acid soils the concentration of toxic Al3+ increases and disturbs root growth and function.
Wheat has adaptation a tolerance to aluminium, releasing that bind to harmful aluminium cations. Sorghum is believed to have the same tolerance mechanism.
Aluminium production possesses its own challenges to the environment on each step of the production process. The major challenge is the emission of greenhouse gases. These gases result from electrical consumption of the smelters and the byproducts of processing. The most potent of these gases are Fluorocarbon, namely CF4 and C2F6, from the smelting process.
Biodegradation of metallic aluminium is extremely rare; most aluminium-corroding organisms do not directly attack or consume the aluminium, but instead produce corrosive wastes. See also the abstract of . The fungus Geotrichum candidum can consume the aluminium in . The bacterium Pseudomonas aeruginosa and the fungus Cladosporium resinae are commonly detected in aircraft fuel tanks that use kerosene-based fuels (not avgas), and laboratory cultures can degrade aluminium.
Production and refinement
+ World's largest producing countries of aluminium, 2024
! Country !! data-sort-type="number" Output
(thousand
tons)43,000 4,200 3,800 3,300 2,700 1,600 1,500 1,300 1,100 870 780 670 6,800 72,000
Bayer process
Bauxite is converted to alumina by the Bayer process. Bauxite is blended for uniform composition and then is ground fine. The resulting slurry is mixed with a hot solution of sodium hydroxide; the mixture is then treated in a digester vessel at a pressure well above atmospheric, dissolving the aluminium hydroxide in bauxite while converting impurities into relatively insoluble compounds:
Hall–Héroult process
The conversion of alumina to aluminium is achieved by the Hall–Héroult process. In this energy-intensive process, a solution of alumina in a molten () mixture of cryolite (Na3AlF6) with calcium fluoride is electrolysis to produce metallic aluminium. The liquid aluminium sinks to the bottom of the solution and is tapped off, and usually cast into large blocks called Bar stock for further processing.
Recycling
Recovery of the metal through recycling has become an important task of the aluminium industry. Recycling was a low-profile activity until the late 1960s, when the growing use of aluminium brought it to public awareness. Recycling involves melting the scrap, a process that requires only 5% of the energy used to produce aluminium from ore, though a significant part (up to 15% of the input material) is lost as dross (ash-like oxide). An aluminium stack melter produces significantly less dross, with values reported below 1%.
Applications
Metal
The global production of aluminium in 2016 was 58.8 million metric tons. It exceeded that of any other metal except iron (1,231 million metric tons).
(2025). 9783527306732, Wiley-VCH. ISBN 9783527306732
Compounds
The great majority (about 90%) of aluminium oxide is converted to metallic aluminium. Being a very hard material (Mohs hardness 9), alumina is widely used as an abrasive; being extraordinarily chemically inert, it is useful in highly reactive environments such as high pressure sodium lamps.The Ceramic Society of Japan (2025). 9784431541080, Springer Science & Business Media. . ISBN 9784431541080 Aluminium oxide is commonly used as a catalyst for industrial processes; e.g. the Claus process to convert hydrogen sulfide to sulfur in refineries and to alkylation . Many industrial Catalysis are catalyst support by alumina, meaning that the expensive Catalysis material is dispersed over a surface of the inert alumina. Another principal use is as a drying agent or absorbent.
(2025). 9789241547659, World Health Organization. ISBN 9789241547659
Biology
Despite its widespread occurrence in the Earth's crust, aluminium has no known function in biology. At pH 6–9 (relevant for most natural waters), aluminium precipitates out of water as the hydroxide and is hence not available; most elements behaving this way have no biological role or are toxic. Aluminium sulfate has an LD50 of 6207 mg/kg (oral, mouse), which corresponds to 435 grams (about one pound) for a mouse.
Toxicity
Aluminium is classified as a non-carcinogen by the United States Department of Health and Human Services. A review published in 1988 said that there was little evidence that normal exposure to aluminium presents a risk to healthy adult, and a 2014 multi-element toxicology review was unable to find deleterious effects of aluminium consumed in amounts not greater than 40 mg/day per kg of body weight. Most aluminium consumed will leave the body in feces; most of the small part of it that enters the bloodstream, will be excreted via urine; nevertheless some aluminium does pass the blood-brain barrier and is lodged preferentially in the brains of Alzheimer's patients.
Evidence published in 1989 indicates that, for Alzheimer's patients, aluminium may act by electrostatically proteins, thus down-regulating genes in the superior temporal gyrus.
Effects
Aluminium, although rarely, can cause vitamin D-resistant osteomalacia, erythropoietin-resistant microcytic anemia, and central nervous system alterations. People with kidney insufficiency are especially at a risk. Chronic ingestion of hydrated aluminium silicates (for excess gastric acidity control) may result in aluminium binding to intestinal contents and increased elimination of other metals, such as iron or zinc; sufficiently high doses (>50 g/day) can cause anemia.
Exposure routes
Food is the main source of aluminium. Drinking water contains more aluminium than solid food; however, aluminium in food may be absorbed more than aluminium from water. Major sources of human oral exposure to aluminium include food (due to its use in food additives, food and beverage packaging, and cooking utensils), drinking water (due to its use in municipal water treatment), and aluminium-containing medications (particularly antacid/antiulcer and buffered aspirin formulations). Dietary exposure in Europeans averages to 0.2–1.5 mg/kg/week but can be as high as 2.3 mg/kg/week. Higher exposure levels of aluminium are mostly limited to Plumber, Masonry, electrical workers, machinists, and Surgeon.
Treatment
In case of suspected sudden intake of a large amount of aluminium, the only treatment is deferoxamine mesylate which may be given to help eliminate aluminium from the body by chelation therapy. Aluminum Toxicity from NYU Langone Medical Center. Last reviewed November 2012 by Igor Puzanov, MD However, this should be applied with caution as this reduces not only aluminium body levels, but also those of other metals such as copper or iron.
Environmental effects
High levels of aluminium occur near mining sites; small amounts of aluminium are released to the environment at coal-fired power plants or Incineration. Aluminium in the air is washed out by the rain or normally settles down but small particles of aluminium remain in the air for a long time.