Product Code Database
Wadsleyite is an orthorhombic mineral with the formula β-(Mg,Fe)2SiO4. It was first found in nature in the Peace River meteorite from Alberta, Canada. It is formed by a phase transformation from olivine (α-(Mg,Fe)2SiO4) under increasing pressure and eventually transforms into spinel-structured ringwoodite (γ-(Mg,Fe)2SiO4) as pressure increases further. The structure can take up a limited amount of other bivalent cations instead of magnesium, but contrary to the α and γ structures, a β structure with the sum formula Fe2SiO4 is not thermodynamically stable. Its cell parameters are approximately a = 5.7 Å, b = 11.71 Å and c = 8.24 Å.
Wadsleyite is found to be stable in the upper part of the Transition Zone of the Earth's Upper mantle between in depth. Because of oxygen atoms not bound to silicon in the Si2O7 groups of wadsleyite, it leaves some oxygen atoms insufficiently bonded. Thus, these oxygens are hydrated easily, allowing for high concentrations of hydrogen atoms in the mineral. Hydrous wadsleyite is considered a potential site for water storage in the Earth's mantle due to the low electrostatic potential of the under bonded oxygen atoms. Although wadsleyite does not contain H in its chemical formula, it may contain more than 3 percent by weight H2O, and may coexist with a hydrous melt at transition zone pressure-temperature conditions. The solubility of water and the density of wadsleyite depend on the temperature and pressure in the Earth. Even though their maximum water storage capabilities might be reduced to about 0.5–1 wt% along the normal geotherm, the transition zone which holds up to 60 vol% wadsleyite could still be a major water reservoir in the Earth's interior. Furthermore, the transformation resulting in wadsleyite is thought to occur also in the shock event when a meteorite impacts the Earth or another planet at very high velocity.
Wadsleyite was first identified by Ringwood and Major in 1966 and was confirmed to be a stable phase by Akimoto and Sato in 1968. The phase was originally known as β-Mg2SiO4 or "beta-phase". Wadsleyite was named for mineralogist Arthur David Wadsley (1918–1969).
Although nominally anhydrous, wadsleyite can incorporate more than 3 percent by weight H2O, which means that it is capable of incorporating more water than Earth's oceans and may be a significant reservoir for H (or water) in the Earth's interior.
Wadsleyite II is a separate spinelloid phase with both a single (SiO4) and double (Si2O7) tetrahedral units. It is a magnesium-iron silicate with variable composition that might occur between the stability regions of wadsleyite and ringwoodite γ-Mg2SiO4, but computational models suggest that at least the pure magnesian form is not stable. One-fifth of the silicon atom is in isolated tetrahedral and four-fifths is in Si2O7 groups so that the structure can be thought of as a mixture of one-fifth spinel and four-fifths wadsleyite.
The wadsleyite minerals generally have a microcrystalline texture and are fractured. Because of small crystal size, detailed optical data could not be obtained; however, wadsleyite is anisotropic with low first-order birefringence colors. It is biaxial with a mean refractive index of n = 1.76 and has a calculated specific gravity of 3.84. In X-ray powder diffraction, its strongest points in pattern are: 2.886(50)(040), 2.691(40)(013), 2.452(100,141), 2.038(80)(240), 1.442(80)(244).
|
|