Tinning is the process of thinly coating sheets of wrought iron or steel with tin, and the resulting product is known as tinplate. The term is also widely used for the different process of coating a metal with solder before soldering.
It is most often used to prevent rust, but is also commonly applied to the ends of stranded wire used as electrical conductors to prevent oxidation (which increases electrical resistance), and to keep them from fraying or unraveling when used in various like twist-ons, , or , where stray strands can cause a short circuit.
While once more widely used, the primary use of tinplate now is the manufacture of . Formerly, tinplate was used for cheap pots, pans, and other holloware. This kind of holloware was also known as tinware and the people who made it were tinplate workers.
The untinned sheets employed in the manufacture are known as black plates. They are now made of steel, either Bessemer process steel or open-hearth. Formerly wrought iron was used, and was of two grades, coke iron and charcoal iron; the latter, being the better, received a heavier coating of tin, and this circumstance is the origin of the terms coke plates and charcoal plates by which the quality of tinplate is still designated, although iron is no longer used. Tinplate was consumed in enormous quantities for the manufacture of the tin cans in which preserved meat, fish, fruit, , , and numerous other products are packed, and also for the household utensils of various kinds made by the tinsmith.
The manufacture of tinplate was long a monopoly of Bohemia, but in about the year 1620 the industry spread to Saxony. Tinplate was apparently produced in the 1620s at a mill of (or under the patronage of) the Earl of Southampton, but it is not clear how long this continued.
Andrew Yarranton, an English engineer and agriculturist, and Ambrose Crowley (a Stourbridge blacksmith and father of the more famous Ambrose Crowley) were commissioned to go to Saxony and if possible discover the methods employed. They visited Dresden in 1667 and found out how it was made. In doing so, they were sponsored by various local and people connected with the project to make the River Stour navigable. In Saxony, the plates were forged, but when they conducted experiments on their return to England, they tried rolling the iron. This led to two of the sponsors, the ironmasters Philip Foley and Joshua Newborough, erecting a new mill, Wolverley Lower Mill (or forge), in 1670. This contained three shops: one being a slitting mill, which would serve as a rolling mill, the others being forges. In 1678 one of these was making and the other drawing out blooms made in elsewhere. It is likely that the intention was to roll the plates and then finish them under a hammer, but the plan was frustrated by one William Chamberlaine renewing a patent granted to him and Dud Dudley in 1662. Yarranton described the patent as "trumped up".
The slitter at Wolverley was Thomas Cooke. Another Thomas Cooke, perhaps his son, moved to Pontypool and worked there for John Hanbury (1664–1734). According to Edward Lhuyd, by 1697, John Hanbury had a rolling mill at Pontypool for making "Pontypoole Plates" machine. This has been claimed as a tinplate works, but it was almost certainly only producing (untinned) blackplate. However, this method of rolling iron plates by means of cylinders, enabled more uniform black plates to be produced than was possible with the old plan of , and in consequence the English tinplate became recognised as superior to the Germany. Tinplate first begins to appear in the Gloucester Port Books (which record trade passing through Gloucester, mostly from ports in the Bristol Channel) in 1725. The tinplate was shipped from Newport, Monmouthshire.Data extracted from D. P. Hussey et al., Gloucester Port Books Database (CD-ROM, University of Wolverhampton 1995). This immediately follows the first appearance (in French language) of Réaumur's Principes de l'art de fer-blanc, and prior to a report of it being published in England.
Further mills followed a few years later, initially in many ironmaking regions in England and Wales, but later mainly in south Wales. In 1805, 80,000 boxes were made and 50,000 exported. The industry continued to spread steadily in England and especially Wales, and after 1834 its expansion was rapid, Great Britain becoming the chief source of the world's supply. In that year her total production was 180,000 boxes of 108 lb each (around 50 kg, in America a box is 100 lb), in 1848 it was 420,000 boxes, in 1860 it reached 1,700,000 boxes. But subsequently the advance was rapid, and the production reached about 2,236,000 lb in 1891. One of the greatest markets was the United States of America, but that market was cut off in 1891, when the McKinley tariff was enacted there. This caused a great retrenchment in the British industry and the emigration to America of many of those who could no longer be employed in the surviving tinplate works.
In 1891, the United States made 11,000 tons of tinplate and imported 325,100 tons, but in 1899, it made 360,900 tons, importing only 63,500 tons (mostly for re-export). British exports were further hindered by the Dingley tariff, which removed the advantage of Welsh plate on America's Pacific coast, had by 1900 increased to more than 849,000,000 lb, of which over 141,000,000 lb were terne-plates. The total imports in that year were only 135,264,881 lb. In later years, again, there was a decline in the American production, and in 1907 only 20% of the American tinplate mills were at work, while the British production reached 14 million boxes.
Despite this blow, the industry continued, but on a smaller scale. Nevertheless, there were still 518 mills in operation in 1937, including 224 belonging to Richard Thomas & Co. However the traditional 'pack mill' had been overtaken by the improved 'strip mill', of which the first in Great Britain was built by Richard Thomas & Co. in the late 1930s. Strip mills rendered the old pack mills obsolete and the last of them closed in about the 1960s.
If the plate is not finished on singles, or without doubling the plate over, it is doubled over in a squeezer. The squeezer was like a table where one half of the surface folds over on top of the other and a press flattens the doubled over plate so the rolled end will fit in the rollers. It is then reheated for another set of rolling. This is repeated until the desired geometry is reached. Note that if the plate needs to be doubled over more than once the rolled end is sheared off. The pack is then allowed to cool. When cool, the pack is sheared slightly undersized from the final dimensions and the plates separated by openers..
At this point, the plates are covered in mill scale and must be pickled. This involves dipping the plates in sulfuric acid for five minutes. The pickling turns the scales into a greenish-black slime which is removed via annealing. The plates are annealed for approximately 10 hours and then allowed to slowly cool. At this point the plates are known as pickled and annealed black plates. These plates were commonly sold for stamping and enameling purposes..
After this, the plates are rough and not straight, so they are cold rolling several times. The rolling lengthens the plates to their final dimension. They are then annealed again to remove any strain hardening. These plates are called black plate pickled, cold rolled, and close annealed (black plate p. cr. and ca.). To attain perfect cleanliness the plates are pickled again in a weak sulfuric acid. Finally they are rinsed and stored in water until ready to be tinned..
The tinning set consists of at least one pot of molten tin, with a zinc chloride flux on top, and a grease pot. The flux dries the plate and prepares it for the tin to adhere. If a second tin pot is used, called the wash pot, it contains tin at a lower temperature. This is followed by the grease pot, which contains oil and a tinning machine. The tinning machine has two small rollers that are spring-loaded together so that when the tinned plate is inserted the rolls squeeze off any excess tin. The springs on the tinning machine can be set to different forces to give different thicknesses of tin. Finally, the oil is cleaned off with fine bran and dusted clean..
What is described here is the process as employed during the 20th century. The process grew somewhat in complexity over time, as it was found that the inclusion of additional procedures improved quality. The practice of hot rolling and then cold rolling evidently goes back to the early days, as the Knight family's tinplate works had (from its foundation in about 1740) two rolling mills, one at Bringewood (west of Ludlow) which made blackplate, and the other the tin mill at Mitton (now part of Stourport, evidently for the later stages.
Tinplate made via hot-dipped tin plating is made by cold rolling steel or iron, pickling to remove any fouling, annealing to remove any strain hardening, and then coating it with a thin layer of tin. Originally this was done by producing individual or small packs of plates, which became known as the pack mill process. In the late 1920s strip mills began to replace pack mills, because they could produce the raw plates in larger quantities and more economically.
In electroplating, the item to be coated is placed into a container containing a solution of one or more tin salts. The item is connected to an electrical circuit, forming the [[cathode]] (negative) of the circuit while an electrode typically of the same metal to be plated forms the [[anode]] (positive). When an [[electric current]] is passed through the circuit, metal [[ion]]s in the solution are attracted to the item. To produce a smooth, shiny surface, the electroplated sheet is then briefly heated above the melting point of tin. Most of the tin-plated steel made today is then further electroplated with a very thin layer of [[chromium]] to prevent dulling of the surface from oxidation of the tin.
|
|